COATINGS · Sulfate process
M-2196 is a rutile titanium dioxide pigment made by the sulfate process, with zirconia/alumina inorganic surface treatment and organic surface treatment, for solvent-based furniture- and industrial-paint evaluation.
Its current technical profile identifies gloss, whiteness with a blue undertone, and wetting and dispersing behavior as priorities for buyer testing. Review the typical data and confirm suitability in your own binder, solvent package, formulation, application, drying or cure, and end-use conditions.
M-2196 is a sulfate-process rutile titanium dioxide pigment with zirconia/alumina and organic surface treatment for solvent-based furniture- and industrial-paint evaluation.
Use M-2196 as a candidate when gloss, whiteness, undertone, wetting and dispersing behavior are relevant to the intended coating system. Final selection should account for binder and solvent system, pigment loading, additives, dispersion process, substrate, film build, application, drying or cure conditions, appearance and destination documents.
Review each documented direction in your own binder, solvent package, formulation, application, drying or cure, and end-use conditions.
Evaluate M-2196 in the intended resin and solvent system, pigment loading, additives, dispersion process, substrate, application and drying or cure conditions. Confirm gloss, whiteness, undertone, wetting, dispersion and finished appearance.
Test M-2196 in the selected industrial coating formulation, substrate preparation, film build, application and drying or cure conditions. Confirm gloss, whiteness, dispersion, coverage and finished-film performance for the intended end use.
Use the documented M-2196 profile and typical data to frame buyer testing.
These evaluation priorities identify what to check during buyer testing. They do not guarantee fixed results.
Review the source-backed values as an input to M-2196 product evaluation.
| Parameter | Value | Test method |
|---|---|---|
| Processing method | Sulfate | - |
| Crystal form | Rutile | - |
| Inorganic surface treatment | ZrO₂, Al₂O₃ | - |
| Organic surface treatment | Yes | - |
| Classification | R2 | ISO 591-1 |
| Color | ΔE ≤ 0.5 | ISO 787-25 |
| Relative scattering power | 95%-105% | ISO 787-24 |
| Density | 4.0 g/cm³ | ISO 787-10 |
| Dispersion in polyester system | ≤27.5 μm | GB/T 21868.3-2008 |
| TiO₂ content | 94% | ISO 591-1 |
| CIE L* | 95.3 | GB/T 1864-2012 |
| Reducing power (TCS) | 1950 | - |
| pH | 7.0 | ISO 787-9 |
| Oil absorption | 19 g/100 g | ISO 787-5 |
| Residue on 45 μm | 0.01% | ISO 787-18 |
| Resistivity | 100 Ω·m | ISO 787-14 |
| Volatiles at 105°C, at packaging | 0.3% | ISO 787-2 |
Confirm suitability in your own formulation and processing conditions.
Request the M-2196 TDSRequest the current M-2196 technical data and describe additional technical or export document needs. Our team will confirm the applicable scope.
Request M-2196 DocumentsSubmitting a request does not confirm that every requested document is available or applicable.
Technical Data Sheet (TDS): Request the current M-2196 technical data for evaluation.
Additional document requirements: Describe type, destination and context. No availability is implied.
Continue to the relevant destination page for procurement, document and inquiry guidance.
These paths do not claim M-2196 registration, compliance, stock or local availability.
Share the coating system, binder, solvent package, additives, application or drying conditions, destination and evaluation objective. Submission does not approve quantity, freight or dispatch timing.
Request an M-2196 Sample